inorganic nano binders |
1.
Inorganic Hybrid Binders
Main Features:
 |
Super- Weathering
(Anti UV)
& Heat Resistance
|
Siloxane (Si-O-Si)
Structure
-- Strong
Ion Bonding
-- Stable for UV & Heat than Organic
Coatings
|
Chemical Structure
|
Bond Energy (Kcal/mole)
|
UV Absorption
Wavelength
|
|
Organic Coating
|
C - O
|
83
|
290-390nm
|
|
C - C
|
83
|
|
C - H
|
98
|
|
Inorganic Coating
|
Si - O
|
101
|
270 nm
|
|
UV Energy
|
>85
|
|
When bond
energy is smaller than UV energy,
The film
structure will be deteriorated by UV irradiation.
Solar Light Wavelength Bands on Earths

 |
Anti Stain, Self
Cleaning Ability (Lotus Effect)
|
| |
|
cilium |
 |
lotus
Effect |
 |
 |
Self Cleaning |
 |
 |
Hard Coat with High
Abrasion Resistance
|
 |
Top Coat for Inorganic &
Organic Substrates
|
Product Data Summary(1)
|
Solution
Properties
|
|
|
SN-506N
|
SN-506AP
|
SN-508
|
SN-602(A)/(B)
|
|
Appearance
|
Light yellow Translucence Solution
|
Translucence Solution
|
|
Main Ingredients
|
SiO2 , Metal oxide
|
SiO2 , Silane
|
|
Other Additives
|
< 1%
|
<1%
|
|
Components
|
1 Pack
|
2 Packs
|
|
PH
|
3 - 6
|
7-9
|
|
Solid content
|
25% min
|
22% min
|
|
Diluent
|
IPA/BCS/NBA
|
IPA/BCS/NBA
|
|
Specific Gravity(25
℃)
|
0.85 - 1.0
|
0.9-1.0
|
|
Viscosity (cp) (25
℃)
|
< 50
|
< 50
|
|
Flash point
|
19℃
|
19℃
|
|
Shelf Life (5-30
℃)
|
6 Months
|
6 Months
|
Product Data Summary(2)
|
Applied Methods
|
|
|
SN-506N
|
SN-506AP
|
SN-508
|
SN-602(A)/(B)
|
|
Finish
|
Gloss
|
Gloss
|
|
Pigmented/Color
|
Can add pigment to
grind
|
Clear coat
|
|
Apply method
|
Spray/
Roller /Dip
|
Spray/
Dip
|
|
Wet Film (W.F.T)
|
40 - 100 µ m
|
25 - 100 µ m
|
|
Dry Film (D.F.T)
|
10-25 µ m
|
5-25 µ m
|
|
Over Coatability
|
Poor
|
NO
|
|
Hardened condition
|
180~200℃ / 20-30 mins.
SN-506AP add SN-505H can make air dry system
|
80℃ / 10-30 mins.
/Post Cure RT
24hrs
|
|
Pot Life(15-25
℃)
|
-
|
< 8 hrs
|
|
Applied Substrates
|
Iron & Non Iron
metals /Wood/
Cements/Stones/glass/ceramic
|
Plastics
|
Product Data Summary(3)
|
Film Properties
|
|
|
SN-506N
|
SN-506AP
|
SN-508
|
SN-602(A)/(B)
|
|
Pencil Hardness
|
4~6H
|
3H
|
|
Weathering
|
E
|
G
|
|
Adhesion
|
E
|
E
|
|
Stain resistance
|
E
|
E
|
|
Heat resistance
|
300~800
℃
|
300
℃
|
|
Gloss
|
E
|
G
|
G
|
|
Scratch Resistance
|
E
|
E
|
E: Excellent, G: Good,
F: Fair, P: Poor
*
Pencil hardness depend on which kind of substrate
and film thickness
Coating Examples
By Inorganic Hybrid Binders
Da- Jiao -Si Temple , Koashiung
|
1. Substrate : concrete, wood,
(1) Primer : SN-100(pearl pigmented)
(2) Top coat : SN-500(clear)
3. Features: Shine & Anti-Stain
|
   |
Qi- Jin
Elementary School, Kaoshiung
|
(1) Primer : SN-100(pigmented)
(2) Top coat : SN -500(clear)
|
   |
Xiao Liu qiu
Island, outside Taiwan
|
(1) Primer :
B-66(Rohm & Hass, Colored)
(2) Top coat : SN -500 (clear)
3. Features: Anti-Stain & Weathering
|
   |
|
|

|
1. Substrate : Cold-Rolled Steel
(2) Top coat : SN -500 (pigmented)
3. Features: Anti-Stain & Scratch-Resistance
|
| |